  • INSPIRED BY TEETH Natural beauty in all forms. Do full contour zirconia prosthetics look natural? Yes! With Zirconia ST-ML light is transmitted in the incisal area and blocked in the cervical area. Giving you the flexibility to make beautifull full contour prothetics - regardless of the abutment color. Ideal for up to 3 units posterior bridges with a...

  • Ultra Translucent Multi Layer Zirconia UT-ML INSPIRED BY ENAMEL  Let natural beauty shine through. Making natural veneers and other anterior prosthetics from zirconia? It’s possible! Viva UT-ML Zirconia is so translucent that light reaches the original tooth color. This zirconia has one of the highest translucency levels on the market, as well as a shade...

  • Viva Multi-Layer (ML) Zirconia blanks - Integrated color shift. Viva ML discs are polychrome high performance zirconia blanks with exceptional constant quality. This polychrome zirconia disc consists of four pre-colored layers showing smooth enamel, dentin and cervical color shifts. A natural tooth restoration can be performed immediately in one step...

  • Highly translucent zirconia Disk  The OPERA SYSTEM® portfolio is even completed by the white Zirconia OPERA SYSTEM® Viva HT (High Translucent) Disc, which gives you additional opportunities for individual staining and veneering.HT discs are also available in HT 2W* shade and HT 3W* Properties :• High translucent zirconia disc • Flexural Strength:...

  • FEATURES: TRANSLUCENCY : 44 % à 47 % FLEXURAL STRENGTH : : 800 à 1100 MPa THERMAL EXPANSION: (25-500°C) : (10.5 ± 1.0) ×10-6·K-1 COMPOSITION: ZrO2+HfO2, Y2O3,  Fe2O3, Al2O3, Er2O3,... SINTERING TEMPERATURE  :  1480°C during 2 hours ReferenceShade - ThicknessDiameterOS VS A1 / 14 A1 - 14 mm 98,5 mm OS VS A1 / 18 A1 - 18  mm 98,5 mm OS VS A1 / 22 A1 - 22...

    0,00 €
    Out of stock
    Add to cart
  • FEATURES: TRANSLUCENCY : 43% 
FLEXURAL STRENGTH : > 1200 Mpa
 THERMAL EXPANSION (25-500°C) : (10.5 ± 1.0) ×10-6·K-1
 COMPOSITION :  Nanometer zirconia powder Fe2O3, Pr2O3, Er2O3, ... 
 SINTERING TEMPERATURE : 1530°C during 2 hours ReferenceShade - ThicknessDiameterOS PS A2 / 10 A2 - 10 mm 98,5 mm OS PS A2 / 14 A2 - 14 mm 98,5 mm OS PS A2 / 18 A2 - 18...

    0,00 €
    Out of stock
    Add to cart
  • FEATURES: • TRANSLUCENCY : 39%• FLEXURAL STRENGTH : > 1200 Mpa• THERMAL EXPANSION (25-500°C) : (10.5 ± 1.0) ×10-6·K-1• COMPOSITION : ZrO2+HfO2, Y2O3, Al2O3, ...• SINTERING TEMPERATURE : 1530°C during 2 hours ReferenceShade - ThicknessDiameterOSW / 10 White - 10 mm 98,5 mm OSW / 14 White - 14 mm 98,5 mm OSW / 18 White - 18 mm 98,5 mm OSW / 22 White  -...

  • Synthetic wax blanks Maximum contour sharpness is guaranteed by the opaque color.Indications: Indications: suited to making lost forms (crowns and bridges) for the casting process,but can also be used for pressing and overpressing.Advantages:• Very easy to mill• Does not smear during milling• Nearly burns out without trace• High opacity• Volumetric...

  • PMMA blanks are suitables for fabrication of temporary crowns & bridges.... Properties : • Flexural Strength: 114 MPa• Vickers hardness: 26,60 HV • E-Module :  2771 MegaPascal • Residual Monomer  <1% • Composition : polymethylmethacrylate pur RéférenceShade - ThicknessDiameterOS 500 50 A1 - 12 mm 98,5 mm OS 500 51 A1 - 14 mm 98,5 mm OS 500 52 A1...

  • Pink blanks can be used to mill high esthetical modeling and functional prosthesis.Indications:  Full dentures,  Partial dentures, Temporary implant denture Properties : • Flexural Strength: 114 MPa• Vickers hardness: 26,60 HV • E-Module :  2771 MegaPascal • Residual Monomer  <1% • Composition : polymethylmethacrylate + pigments RéférenceShade -...

  • Produced of 100% organic material. RéférenceShade - ThicknessDiameterOS 500 70 Transparent - 12 mm 98,5 mm OS 500 71 Transparent - 14 mm 98,5 mm OS 500 72 Transparent - 18 mm 98,5 mm OS 500 73 Transparent - 20 mm 98,5 mm OS 500 74 Transparent - 25 mm 98,5 mm Restorative materials Opera System® are class IIa medical devices comply with Directive 93/42 EEC....

  • For verifying frameworks on plaster model before final milling. Burns-out without any residual ash. Produced of 100% organic material. RéférenceShade - ThicknessDiameterOS 500 01 Transparent - 12 mm 98,5 mm OS 500 02 Transparent - 14 mm 98,5 mm OS 500 03 Transparent - 18 mm 98,5 mm OS 500 04 Transparent - 20 mm 98,5 mm OS 500 05 Transparent - 25 mm 98,5...

Showing 1 - 12 of 16 items